SWD8008 meji paati cathodic disbonding irin
Ọja ẹya ara ẹrọ ati awọn anfani
* pọ si agbara alemora pẹlu sobusitireti irin
* o tayọ anticorrosion ati yiya resistance
* o tayọ cathodic disbonding resistance
* o tayọ mabomire & ọrinrin resistance
* iduroṣinṣin iduroṣinṣin si iyipada iwọn otutu
* ni ibamu pẹlu fiimu ti a bo ni atẹle
* yago fun ipata ati ipata ati mu igbesi aye iṣẹ pọ si
* Iwọn agbegbe giga lati ṣafipamọ idiyele
Awọn iwọn ohun elo
Iboju Anticorrosion fun eyikeyi awọn ẹya irin, irin alagbara, dada aluminiomu.Kekere dada itọju pẹlu ipata lori irin be.
ọja alaye
| Nkan | A paati | B paati |
| Ifarahan | ina ofeefee omi | awọ adijositabulu |
| Walẹ kan pato (g/m³) | 1.03 | 1.25 |
| Irisi (cps) @ 25 ℃ | 210 | 380 |
| Akoonu to lagbara (%) | 65% | 65% |
| Ipin idapọ (nipa iwuwo) | 1 | 1 |
| Akoko gbigbẹ oju (h) | wakati 1-3 | |
| Àárí àtúnṣe (h) | min 3 wakati;o pọju wakati 24 (20℃) | |
| Iṣeduro imọ-jinlẹ (DFT) | 0.12kg / ㎡ fiimu sisanra 50μm | |
Aṣoju ti ara-ini
| Nkan | Igbeyewo bošewa | Esi |
| Agbara fifẹ (irin dada gbigbe) Mpa | ASTM D-3359 | 11.5 (tabi sobusitireti ti bajẹ) |
| Idaabobo ipa (kg.cm) | GB/T 1732 | 60 |
| Abrasion resistance (750g/500r) mg | GB/T 1732 | 11 |
| Iwọn otutu iyatọ resistance (-40 + 180 ℃) 24h | GB / 9278-1988 | Deede |
| Idaabobo itusilẹ Cathodic [1.5v, (65 ± 5) ℃, 48h] | HG/T 3831-2006 | ≤15mm |
| Ìwọ̀n g/cm3 | GB/T 6750-2007 | 1.08 |
Idaabobo kemikali
| Acid resistance 50% H2SO4 tabi 15% HCI,30d | ko si ipata, ko si nyoju, ko si Peeli pa |
| Idaduro Alkali 50% NaOH, 30d | ko si ipata, ko si nyoju, ko si Peeli pa |
| Iyọ resistance 60g/L, 30d | ko si ipata, ko si nyoju, ko si Peeli pa |
| Iyọ sokiri resistance 1000h | ko si ipata, ko si nyoju, ko si Peeli pa |
| Idaabobo epo, 0 # Diesel, epo robi, 30d | ko si ipata, ko si nyoju, ko si Peeli pa |
| (Fun itọkasi: San ifojusi si ipa ti fentilesonu, asesejade ati idasonu. Idanwo immersion ominira ni a ṣe iṣeduro ti o ba nilo data miiran pato) | |